AZO Coated Glass
• Produce Code - AZOSE
• Resistivity - ≤ 10 ohms/sq.
• Transmittance - ≥ 81%
• Coating Thickness - 850 nm
• Substrate Thickness - 3.2 mm
• Maximum operating temperature is 600 °C.
• Made for LCD's, RF-EMI shielding, solar cell fabrication, optoelectronic devices, photovoltaics, etc.
AZO Coated Glass Specifications and Details
The Aluminium doped Zinc oxide (AZO) coated glass is a transparent conductive oxide (TCO) over a soda-lime glass substrate. It has manufactured by using target sputtering method. It is a transparent conductive glass substrate with transmittance greater than 81%. The AZO coated glass is a single side coated slides, whereas the other side is insulated. It is not easy to identify the conductive side with bare eyes. It is suggested to a used multimeter or four-probe method to confirm the coated side.
Dimensions & other details
The AZO coating or layer thickness is 800 - 850nm, and the resistivity is around 10 ohms/sq.cm. The surface of the substrate is quite smooth, but the surface roughness (RMS) is 2nm. The maximum size produced is 304.8mm x 304.8mm in a 3.2mm plate thickness. Our standard sizes are 25mm x 25mm, 50mm x 25mm, 50mm x 50mm, 75mm x 25mm, and 100mm x 100mm. The uniformity of resistance and Haze is less than 10%. It is beneficial for heating applications since its maximum operating temperature is 600 °C.
The AZO coated glass is less popular as compared to ITO and FTO glass, but it is the best economical option for many applications. It is mainly utilized in the LCD's, RF-EMI shielding, solar cell fabrication, optoelectronic devices, photovoltaics, etc.
We produce and supply uniform AZO coating at Shilpa Enterprises, whereas a patterning or etching service for this product is discontinued. We also offer customized dimensions on demand. Download the datasheet for more technical specification details.