Features Magnesium : 60.29 Oxygen : 39.67 Melting Point : 2852 °C/5166 °F Boiling Point : 3600 °C (6512 °F) Density : 3.58 g/cm3 0.129 lb/in3 Molar Mass : 40.30 g/mol       Chemical...

Main Features Efficient electrical conductivity Optimal transparency Uniform coating Lower electrical resistance Excellent electromagnetic shielding properties Thermally/chemically stable product

Main Features High-quality polished fused quartz material Optimal purity of the material Highly precise laser cut quartz discs with accurate dimensions Smoothed edges to prevent cuts when handling Customized industrial/research grade quartz discs

Technical Specifications Concentration: 20 wt. % in isopropanol Particle Size: < 50 nm (DLS) pH Level: 8 - 10 Density: 0.79 g/cm3 at 25 °C Mechanical Strength: 300 - 630 MPa Compressive Strength: 2,000 - 4,000 MPa Hardness: 15 - 19 GPa Moderate Thermal Conductivity: 20 - 30...

Main Features Top-quality raw quartz used to make end-product Stringent quality measures ensure maximum purity of the material Advanced procuring and processing involved to furnish a constant industrial-grade quality Ground edges to prevent accidental cuts Customized dimensions and specifications followed for...

Main Features and Benefits Its highly conductive. Excellent optical transmittance. Made for many optoelectronic applications. Typically the transmittance at 550nm is more than 80%. Haze is around 9%. FTO coating's maximum operating temperature is 450 °C FTO7Y Resistivity - 7 ohms/sq. &...

Technical Specifications Chemical Formula: TiO2 Particle Size: <100 nm Density: 4.26 g/cm3 Color: White Opacity: High Crystal Structure: Rutile or Anatase Bandgap: 3.0 eV Photostability: Good Toxicity: Low

Main Features High-quality, purest silica used for fabricating Extremely strong and durable Remarkably inert with excellent corrosion-resistivity Lower coefficient of thermal expansion Excellent range of optical transmission

Features High-end, fine-quality polyester film Excellent transmittance power Enhanced resistance characteristics Precise ITO coating improves substrate strength, durability, and quality Easily connectable using conductive inks, conductive adhesives/paints, and many more Excellent for EMI-shielding...

Main Highlights Size: 1 to 100 nm Shape: Spherical, Cubic, or Hexagonal Composition: Magnetite (Fe3O4) or Maghemite (γ-Fe2O3) Magnetic properties: Superparamagnetic Biocompatibility: Non-toxic to living cells Surface area: 100 to 1000 m2/gm Bulk density: 0.5 to 1.0 gm/cm3 Melting...

Main Features High-quality, purest silica used for fabricating Extremely strong and durable Remarkably inert with excellent corrosion-resistivity Lower coefficient of thermal expansion Excellent range of optical transmission

Main Features Product Name: ITO Coated PEN sheet Resistivity - 12 ohms/sq Dimension - 290mm x 210mm & 100mm x 100mm Sheet Thickness - 0.125 mm ITO layer thickness - >150nm Transmittance > 75% Haze - 2% Surface Roughness - less than 1

Technical Specifications Chemical formula: CuO Appearance: Black to brown powder Average particle size: 1-30 nm Specific surface area: 100-200 m2/g Melting point: 1201°C (2194 °F) Boiling point: 2000 °C (3632 °F) Density: 6.31 g/cm3 Electrical conductivity: 1.0-2.08 eV ...

Features Quartz Fiber Diameter 3-5um Silica Content si02≧99.97% Heat conductivity coefficient - 0.01 ——0.029kilocalorie\M c End-use temperature ：Under 1700 ℃ The moisture content: ≤0.4% ignition loss ≤0.1% Strength of raw silk fracture >0.05N/TEX Natural capacity degrees 5-6KG\cubic ...

Features Surface Resistivity – < 1 Ohms/Sq. Coating Thickness – 500 nm Substrate Thickness – 0.8 mm, 2.0 mm Transmittance – Null Coating – One-sided Customization – Available

Technical Specifications Molecular weight: 60.0843 g/mol Boiling point: 2230°C Density: 2.65 g/cm³ Electrical resistivity: 10^5 to 10^18 Ωm Appearance: Clear Electronegativity: 1.90 The heat of fusion: N/A The heat of vaporization: N/A Thermal conductivity: 1.3 W/mK at room...

Features Size: Nanoscale Zinc: 80.34 Oxygen: 19.6 Melting point: 1975 °C or 3587 °F Boiling point: 2360 °C or 4280 °F Density: 5600 kg/m3 or 0.202 lb./in3 Molar Mass: 81.40 g/mol Form: Powder Colour: White pH value: 8.9 Surface treating compound: Amphoteric...

Main Features High-efficiency sheet/film/glass coatings Advanced electron beam coating method used Excellent level of resistance, absorbance, transmittance, and reflectance of the substrate Customized coating pattern and thickness achievable Multiple coating options available Constant high-end product...

Features Composition: Silicon - Oxygen Melting Point: 1710 °C Boiling Point: 2950 °C Density: Variable (2.2-2.65 g/cm³) Purity: High (Above 99%) Synthesis Process: Controlled methods Structure: Crystal lattice Average Particle Size: 20-50 nm SSA: ~220 m2/g Molecular...

Main Highlights Produce Code - AZOSE Resistivity - ≤ 10 ohms/sq. Transmittance - ≥ 81% Coating Thickness - 850 nm Substrate Thickness - 3.2 mm Maximum operating temperature is 600 °C. Made for LCD's, RF-EMI shielding, solar cell fabrication, optoelectronic devices, photovoltaics, etc.